Filifiliga Tele mo Saina E-Glass, Glass Fiber Direct Roving mo le LFT Process

Filifiliga Tele mo Saina E-Glass, Glass Fiber Direct Roving mo le LFT Process Ata Fa'aalia
  • Filifiliga Tele mo Saina E-Glass, Glass Fiber Direct Roving mo le LFT Process
  • Filifiliga Tele mo Saina E-Glass, Glass Fiber Direct Roving mo le LFT Process
  • Filifiliga Tele mo Saina E-Glass, Glass Fiber Direct Roving mo le LFT Process
  • Filifiliga Tele mo Saina E-Glass, Glass Fiber Direct Roving mo le LFT Process

fa'amatalaga pu'upu'u:

O le Direct Roving ua ufiufiina i le lapopo'a e fa'avae i le silane e fetaui ma le unsaturated polyester, vinyl ester ma le epoxy resins ma ua mamanuina mo le winding o le filament, pultrusion ma le lalagaina.

MOQ:10 tone


Fa'amatalaga o le oloa

Fa'ailoga o Oloa


Faatasi ai ma le filosofia faapisinisi "Client-Oriented", o se faiga faigata o le pulea lelei o le lelei, meafaigaluega gaosiga faigata ma se aufaigaluega R&D malolosi, matou te ofoina atu oloa sili ona lelei, fofo sili ona lelei ma tau taugofie mo le Tele Selection mo Saina E-Glass, Glass Fiber Direct Roving mo le LFT Process, O le manatu o la matou kamupani o le "Faamaoni, Saosaoa, Auaunaga, ma le Fiafia". O le a matou mulimuli i lenei manatu ma maua le tele o le faamalieina o tagata faatau.
Fa'atasi ai ma le filosofia fa'apisinisi "Client-Oriented", o se faiga faigata o le pulea lelei, meafaigaluega gaosiga fa'apitoa ma se 'aufaigaluega R&D malolosi, matou te ofoina atu oloa sili ona lelei, auaunaga sili ona lelei ma tau taugofie moFemalagaa'i a le Gmt Saina, fealua'i sa'o i luga o le fiberglass, O le igoa o le Kamupani, e masani ona faʻamuamua le lelei o le faavae o le kamupani, sailia le atinaʻe e ala i le maualuga o le talitonuga, usitaʻia ma le faʻamaoni tulaga faʻatonuina o le ISO, ma fausia ai le kamupani sili ona maualuga i le agaga o le faʻamaoni ma le faʻamoemoe.

MEATOTINO

• Uiga lelei i le fa'agasologaina, e itiiti le fa'apupulaina.
• Fegalegaleai ma le tele o resin.
• Vave ma atoatoa le susu ese.
• Uiga lelei fa'amekanika o vaega ua mae'a.
• Tete'e lelei tele i le 'ele o vaila'au fa'akemikolo.

TALOSAGA

• E talafeagai le 386T mo le faʻaaogaina i paipa, ipu mamafa, uʻamea ma faʻataʻitaʻiga, ma o uʻamea lalagaina ua liua mai ai e faʻaaogaina i vaʻa ma tane e teu ai vailaʻau.

FA'AILOGA

 Ituaiga Tioata

E6

 Ituaiga o le Tele

Silane

 Fa'ailoga o le Tele

386T

Fa'asologa o le Mamafa((tex)

300

200

400

200

600

735

900

1100

1200

2000

2200

2400

4800

9600

Lapoa o le Filament (μm)

13

16

17

17

17

21

22

24

31

FA'AMATALAGA FA'ATEKINIKA

Fa'asologa o le Mamafa (%)  Aotelega o le Susū (%)  Tele o le anotusi (%)  Malosiaga o le Malepelepe (N/Tex )
ISO 1889 ISO3344 ISO1887 ISO3341
± 5 ≤ 0.10 0.60 ± 0.10 ≥0.40（≤2400tex）≥0.35（2401~4800tex）≥0.30（>4800tex）

MEAFAIGALUEGA FA'AMEKANIKA

 Meatotino Fa'amekanika

 Iunite

 Taua

 Resin

 Metotia
 Malosiaga o le Fetaia'i

MPa

2660

UP

ASTM D2343
 Modulus o le Tete'e

MPa

80218

UP

ASTM D2343
 Malosi o le sele

MPa

2580

EP

ASTM D2343
 Modulus o le Tete'e

MPa

80124

EP

ASTM D2343
 Malosi o le sele

MPa

68

EP

ASTM D2344
 Taofia le malosi o le sele (72 itula o le fa'apuna)

%

94

EP

/

Fa'amatalaga:O faʻamaumauga o loʻo i luga o tau faʻataʻitaʻi moni ia mo le E6DR24-2400-386H ma mo naʻo le faʻasinomaga.

ata4.png

AFIFIINA

 Maualuga o le afifi mm (in) 255(10) 255(10)
 Lapoa i totonu o le afifi mm (in) 160 (6.3) 160 (6.3)
 Lapo'a i fafo o le afifi mm (in) 280(11) 310 (12.2)
 Mamafa o le afifi kg (lb) 15.6 (34.4) 22 (48.5)
 Numera o vaega 3 4 3 4
 Numera o doffs i le vaega taʻitasi 16 12
Numera o laupapa doff i le paleti 48 64 36 48
Mamafa mama i le pallet kg (lb) 750 (1653.5) 1000 (2204.6) 792 (1746.1) 1056 (2328.1)
 Umi o le paleti mm (in) 1120 (44.1) 1270 (50.0)
 Laʻutele o le paleti mm (in) 1120 (44.1) 960 (37.8)
 Maualuga o le paleti mm (in) 940 (37.0) 1200 (47.2) 940 (37.0) 1200 (47.2)

TEUINA

• Se'i vagana ua fa'amaoti mai se isi fa'atonuga, e tatau ona teuina oloa fiberglass i se nofoaga mago, malūlū ma e le susu.

• E tatau ona tu'u pea oloa fiberglass i totonu o latou afifi muamua se'ia o'o i le taimi e fa'aaogaina ai. E tatau ona tausia pea le vevela ma le susū o le potu i le -10℃~35℃ ma le ≤80%.

• Ina ia mautinoa le saogalemu ma aloese mai le faaleagaina o le oloa, e le tatau ona faaputuina paleti i ni vaega e sili atu ma le tolu le maualuga.

• A fa'aputuina pallets i ni vaega se 2 pe 3, e tatau ona fa'aeteete fa'apitoa ina ia sa'o ma sologa lelei le fa'agaoioiga o le pallet pito i luga. Fa'atasi ai ma le filosofia fa'apisinisi "Client-Oriented", o se faiga faigata o le pulea lelei, meafaigaluega gaosiga fa'apitoa, ma se 'aufaigaluega R&D malolosi, matou te ofoina atu oloa sili ona lelei, fofo sili ona lelei, ma tau fa'atauva'a mo le Tele Selection mo Saina E-Glass, Glass Fiber Direct Roving mo le LFT Process, O le manatu o la matou fa'alapotopotoga o le "Fa'amaoni, Saosaoa, Tu'uina atu, ma le Fa'amalieina". O le a matou mulimulita'i i lenei manatu ma maua le fa'amalieina o tagata fa'atau.
O le tele o filifiliga mo le fiberglass Roving Saina, Chopped Strands, e masani ona fa'amuamua le lelei o le fa'avae o le kamupani, e sailia le atina'e e ala i le maualuga o le fa'atuatuaina, usita'ia ma le fa'amaoni tulaga fa'atonutonu o le lelei a le ISO, ma fausia ai le kamupani sili ona maualuga i le agaga o le fa'amaoni ma le fa'amoemoe.

  • Muamua:
  • Sosoo ai:

    • Oloavaega